HJ-606 composite iron titanium anti-rust pigment

[Features]

◆Solve the problem of easy foaming of the current products

◆ Compared with current products, it has better anti-rust performance and more cost-effective

◆ Easy to disperse in paint making process, the finished paint has good anti-precipitation and storage stability

◆ Does not contain harmful heavy metals such as lead and chromium, which is a non-toxic and harmless green product

◆Can replace the conventional anti-rust paints such as chrome, zinc phosphate and aluminum tripolypjsphate, the cost is significantly lowered and the quality won’t be impacted.

[Principle]

◆P₂O₅ has a stronger clelating force on FO₃ ion and various metal ions, forming an excellent passive film on the object and have a strong corrosion inhibition on the corrosion of steel and light metal;

◆ Through the powder surface coating treatment, the combination and dispersion of the pigment and resin-based material has been improved;

◆ Conduct hybrid powder processing by using nano-material, enhance the density of painting film, reduce the permeability and effectively block the erosion of water and oxygen on metal surface.

[Chemical composition]Phosphate, nano-SiO₂, coupling agent

[Applications]

Applicable to all types of solvent-based anti-rust paint, anticorrosive paint and bottom paint

[Product specification]

Appearance iron White powder

P₂O₅, % ≥ 12

Oil absorption, % ≤ 22

Density (27 ℃), g/cm³ 2.8～3.5

PH value of aqueous suspension 7 ~ 10

Volatile (105 ℃) ≤ 1

Sieve residue (600 mesh),% ≤ 1

[Coating performance indicators] Take the alkyd paint of HJ series anti-rust pigment production as an example

Paint color and appearance In line with international color card color, with smooth surface

Drying time (25 ℃), h surface dry ≤ 2, actual dry ≤ 24

Adhesion (the grid method), Grade 1

Impact strength, cm 50

Flexibility, mm 1

Salt resistance water (3% NaCI), h ≥ 360, no foaming, non-rust

Salt resistant spray, h ≥ 240, no foaming, non-rust

[Using methods]: Directly blend with the base materials, auxiliary materials, additives and solvent; just disperse it.

[Recommended dosage]:20-40%, the specific dosage should be confirmed according to product requirements after the test.

[Packing]: Double plastic bag packing 25kg / bag

[Storage]: Keep in ventilated dry place, storage for two years without deterioration.